waste wood from mulberry (#951)
ID-number | #951 |
---|---|
Material | waste wood from mulberry |
Classification | ECN Phyllis classification ▸ untreated wood ▸ other hard wood |
NTA 8003 classification ▸ [100] hout ▸ [110] vers hout ▸ [120] loofhout ▸ [125] hard loofhout | |
Submitter organisation | ECN (Netherlands) |
Remarks | Lignin was extracted with sulphuric acid according to Japanese Industrial Standard. Mulberry wool contains 27% lignin and 73% holocellulose |
Literature | M. Sadakata, K. Takahashi, M. Saito and T. Sakai: Production of fuel gas and char from wood, lignin and holocellulose by carbonization. Fuel 66 (12) pp. 1667-1671 (1987). |
Values
Property | Unit | Value | Std dev | Det lim | Lab | Date | Method | Remarks | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
ar | dry | daf | ||||||||||||||||||
Main biomass properties |
||||||||||||||||||||
Proximate analysis |
||||||||||||||||||||
Moisture content | wt% (ar) | |||||||||||||||||||
Ash content | wt% | 2.50 | ||||||||||||||||||
Ultimate analysis (macroelements) |
||||||||||||||||||||
Carbon | wt% | 47.90 | 49.13 | Measured | ||||||||||||||||
Hydrogen | wt% | 5.90 | 6.05 | Measured | ||||||||||||||||
Oxygen | wt% | 39.40 | 40.41 | Measured | ||||||||||||||||
Sulphur | wt% | 0.40 | 0.41 | Measured | ||||||||||||||||
Total (with halides) | wt% | 96.10 | 96.00 | Calculated | ||||||||||||||||
Heating value |
||||||||||||||||||||
Net calorific value (LHV) | MJ/kg | 18.71 | 19.19 | |||||||||||||||||
Gross calorific value (HHV) | MJ/kg | 20.00 | 20.51 | |||||||||||||||||
HHVMilne | MJ/kg | 19.40 | 19.89 | Calculated |