wood, alder + fir sawdust (#807)
| ID-number | #807 |
|---|---|
| Material | wood, alder + fir sawdust |
| Classification | ECN Phyllis classification ▸ untreated wood ▸ others |
| NTA 8003 classification ▸ [100] hout ▸ [110] vers hout ▸ [115] zaagsel | |
| Ash type | ASTM D1102; 600 oC |
| Submitter organisation | ECN (Netherlands) |
| Remarks | Tacoma, WA, sawdust, sawmill residues. Hazen |
| Literature | T. R. Miles, T. R. Miles,Jr, L. Baxter, R. W. Bryers, B. M. Jenkins and L. L. Oden: Alkali deposits found in biomass power plants. A preliminary investigation of their extend and nature, NREL/TP-433-8142, 82 p. (1995). |
Values
| Property | Unit | Value | Std dev | Det lim | Lab | Date | Method | Remarks | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ar | dry | daf | ||||||||||||||||||
Main biomass properties |
||||||||||||||||||||
Proximate analysis |
||||||||||||||||||||
| Moisture content | wt% | 52.63 | ||||||||||||||||||
| Ash content | wt% | 1.96 | 4.13 | |||||||||||||||||
| Volatile matter | wt% | 36.27 | 76.56 | 79.86 | ||||||||||||||||
| Fixed carbon | wt% | 9.15 | 19.31 | 20.14 | Calculated | |||||||||||||||
Ultimate analysis (macroelements) |
||||||||||||||||||||
| Carbon | wt% | 24.17 | 51.02 | 53.22 | Measured | |||||||||||||||
| Hydrogen | wt% | 2.75 | 5.80 | 6.05 | Measured | |||||||||||||||
| Oxygen | wt% | 18.25 | 38.52 | 40.18 | Calculated | |||||||||||||||
| Nitrogen | wt% | 0.22 | 0.46 | 0.48 | Measured | |||||||||||||||
| Sulphur | wt% | 0.02 | 0.05 | 0.05 | Measured | |||||||||||||||
| Total (with halides) | wt% | 100.00 | 100.00 | 100.00 | Calculated | |||||||||||||||
Halides |
||||||||||||||||||||
| Chlorine (Cl) | mg/kg | 94.7 | 200.0 | 208.6 | Measured | |||||||||||||||
Heating value |
||||||||||||||||||||
| Net calorific value (LHV) | MJ/kg | 7.77 | 19.11 | 19.93 | ||||||||||||||||
| Gross calorific value (HHV) | MJ/kg | 9.65 | 20.38 | 21.25 | ||||||||||||||||
| HHVMilne | MJ/kg | 9.63 | 20.33 | 21.21 | Calculated | |||||||||||||||
Ash Properties |
||||||||||||||||||||
Ash composition |
||||||||||||||||||||
| CO2 | wt% (ash) | 1.85 | ||||||||||||||||||
| SO3 | wt% (ash) | 0.78 | ||||||||||||||||||
| P2O5 | wt% (ash) | 1.90 | ||||||||||||||||||
| SiO2 | wt% (ash) | 35.36 | ||||||||||||||||||
| Fe2O3 | wt% (ash) | 7.62 | ||||||||||||||||||
| Al2O3 | wt% (ash) | 11.54 | ||||||||||||||||||
| CaO | wt% (ash) | 24.90 | ||||||||||||||||||
| MgO | wt% (ash) | 3.81 | ||||||||||||||||||
| Na2O | wt% (ash) | 1.71 | ||||||||||||||||||
| K2O | wt% (ash) | 5.75 | ||||||||||||||||||
| TiO2 | wt% (ash) | 0.92 | ||||||||||||||||||