wood, fir mill waste (#804)
| ID-number | #804 |
|---|---|
| Material | wood, fir mill waste |
| Classification | ECN Phyllis classification ▸ untreated wood ▸ fir/pine/spruce |
| NTA 8003 classification ▸ [100] hout ▸ [110] vers hout ▸ [130] naaldhout ▸ [131] naaldhout | |
| Ash type | ASTM D1102; 600 oC |
| Submitter organisation | ECN (Netherlands) |
| Remarks | Tacoma, WA, Douglas Fir sawmill residues. Hazen. |
| Literature | T. R. Miles, T. R. Miles,Jr, L. Baxter, R. W. Bryers, B. M. Jenkins and L. L. Oden: Alkali deposits found in biomass power plants. A preliminary investigation of their extend and nature, NREL/TP-433-8142, 82 p. (1995). |
Values
| Property | Unit | Value | Std dev | Det lim | Lab | Date | Method | Remarks | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ar | dry | daf | ||||||||||||||||||
Main biomass properties |
||||||||||||||||||||
Proximate analysis |
||||||||||||||||||||
| Moisture content | wt% | 63.00 | ||||||||||||||||||
| Ash content | wt% | 0.15 | 0.41 | |||||||||||||||||
| Volatile matter | wt% | 30.38 | 82.11 | 82.45 | ||||||||||||||||
| Fixed carbon | wt% | 6.47 | 17.48 | 17.55 | Calculated | |||||||||||||||
Ultimate analysis (macroelements) |
||||||||||||||||||||
| Carbon | wt% | 18.96 | 51.23 | 51.44 | Measured | |||||||||||||||
| Hydrogen | wt% | 2.21 | 5.98 | 6.00 | Measured | |||||||||||||||
| Oxygen | wt% | 15.58 | 42.10 | 42.27 | Calculated | |||||||||||||||
| Nitrogen | wt% | 0.02 | 0.06 | 0.06 | Measured | |||||||||||||||
| Sulphur | wt% | 0.01 | 0.03 | 0.03 | Measured | |||||||||||||||
| Total (with halides) | wt% | 100.00 | 100.00 | 100.00 | Calculated | |||||||||||||||
Halides |
||||||||||||||||||||
| Chlorine (Cl) | mg/kg | 703.0 | 1 900.0 | 1 907.8 | Measured | |||||||||||||||
Heating value |
||||||||||||||||||||
| Net calorific value (LHV) | MJ/kg | 5.53 | 19.12 | 19.19 | ||||||||||||||||
| Gross calorific value (HHV) | MJ/kg | 7.56 | 20.42 | 20.50 | ||||||||||||||||
| HHVMilne | MJ/kg | 7.52 | 20.31 | 20.40 | Calculated | |||||||||||||||
Ash Properties |
||||||||||||||||||||
Ash composition |
||||||||||||||||||||
| CO2 | wt% (ash) | 18.92 | ||||||||||||||||||
| SO3 | wt% (ash) | 2.93 | ||||||||||||||||||
| P2O5 | wt% (ash) | 2.87 | ||||||||||||||||||
| SiO2 | wt% (ash) | 15.17 | ||||||||||||||||||
| Fe2O3 | wt% (ash) | 6.58 | ||||||||||||||||||
| Al2O3 | wt% (ash) | 3.96 | ||||||||||||||||||
| CaO | wt% (ash) | 11.90 | ||||||||||||||||||
| MgO | wt% (ash) | 4.59 | ||||||||||||||||||
| Na2O | wt% (ash) | 23.50 | ||||||||||||||||||
| K2O | wt% (ash) | 7.00 | ||||||||||||||||||
| TiO2 | wt% (ash) | 0.27 | ||||||||||||||||||