wood, oak, red, sawdust (#803)
| ID-number | #803 |
|---|---|
| Material | wood, oak, red, sawdust |
| Classification | ECN Phyllis classification ▸ untreated wood ▸ oak |
| NTA 8003 classification ▸ [100] hout ▸ [110] vers hout ▸ [115] zaagsel | |
| Ash type | ASTM D1102; 600 oC |
| Submitter organisation | ECN (Netherlands) |
| Remarks | Red Oak Sawdust, Pennsylvania, clean and dry fines, sawdust. Hazen |
| Literature | T. R. Miles, T. R. Miles,Jr, L. Baxter, R. W. Bryers, B. M. Jenkins and L. L. Oden: Alkali deposits found in biomass power plants. A preliminary investigation of their extend and nature, NREL/TP-433-8142, 82 p. (1995). |
Values
| Property | Unit | Value | Std dev | Det lim | Lab | Date | Method | Remarks | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ar | dry | daf | ||||||||||||||||||
Main biomass properties |
||||||||||||||||||||
Proximate analysis |
||||||||||||||||||||
| Moisture content | wt% | 11.45 | ||||||||||||||||||
| Ash content | wt% | 0.27 | 0.31 | |||||||||||||||||
| Volatile matter | wt% | 76.35 | 86.22 | 86.49 | ||||||||||||||||
| Fixed carbon | wt% | 11.93 | 13.47 | 13.51 | Calculated | |||||||||||||||
Ultimate analysis (macroelements) |
||||||||||||||||||||
| Carbon | wt% | 44.24 | 49.96 | 50.12 | Measured | |||||||||||||||
| Hydrogen | wt% | 5.24 | 5.92 | 5.94 | Measured | |||||||||||||||
| Oxygen | wt% | 38.75 | 43.76 | 43.90 | Calculated | |||||||||||||||
| Nitrogen | wt% | 0.03 | 0.03 | 0.03 | Measured | |||||||||||||||
| Sulphur | wt% | 0.01 | 0.01 | 0.01 | Measured | |||||||||||||||
| Total (with halides) | wt% | 99.99 | 99.99 | 99.99 | Calculated | |||||||||||||||
Halides |
||||||||||||||||||||
| Chlorine (Cl) | mg/kg (dry) | 100.0 | ||||||||||||||||||
Heating value |
||||||||||||||||||||
| Net calorific value (LHV) | MJ/kg | 15.82 | 18.19 | 18.24 | ||||||||||||||||
| Gross calorific value (HHV) | MJ/kg | 17.25 | 19.48 | 19.54 | ||||||||||||||||
| HHVMilne | MJ/kg | 17.36 | 19.60 | 19.66 | Calculated | |||||||||||||||
Ash Properties |
||||||||||||||||||||
Ash composition |
||||||||||||||||||||
| CO2 | wt% (ash) | 14.30 | ||||||||||||||||||
| SO3 | wt% (ash) | 2.69 | ||||||||||||||||||
| P2O5 | wt% (ash) | 1.33 | ||||||||||||||||||
| SiO2 | wt% (ash) | 20.97 | ||||||||||||||||||
| Fe2O3 | wt% (ash) | 2.94 | ||||||||||||||||||
| Al2O3 | wt% (ash) | 2.99 | ||||||||||||||||||
| CaO | wt% (ash) | 10.90 | ||||||||||||||||||
| MgO | wt% (ash) | 4.15 | ||||||||||||||||||
| Na2O | wt% (ash) | 1.40 | ||||||||||||||||||
| K2O | wt% (ash) | 22.40 | ||||||||||||||||||
| TiO2 | wt% (ash) | 0.27 | ||||||||||||||||||