Main biomass properties
|
|
Trace elements composition
|
| |
Aluminium (Al) |
mg/kg
(dry)
|
45 300.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Arsenic (As) |
mg/kg
(dry)
|
33.6 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3683 (modified), EPA 200.8 (ICP-QMS/SFMS) |
| |
Boron (B) |
mg/kg
(dry)
|
97.2 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Barium (Ba) |
mg/kg
(dry)
|
1 720.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Beryllium (Be) |
mg/kg
(dry)
|
1.2 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Calcium (Ca) |
mg/kg
(dry)
|
167 000.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Cadmium (Cd) |
mg/kg
(dry)
|
5.8 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3683 (modified), EPA 200.8 (ICP-QMS/SFMS) |
| |
Cobalt (Co) |
mg/kg
(dry)
|
18.9 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3683 (modified), EPA 200.8 (ICP-QMS/SFMS) |
| |
Chromium (Cr) |
mg/kg
(dry)
|
129.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Copper (Cu) |
mg/kg
(dry)
|
134.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3683 (modified), EPA 200.7 (ICP-AES) |
| |
Iron (Fe) |
mg/kg
(dry)
|
32 500.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Mercury (Hg) |
mg/kg
(dry)
|
0.8 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3683 (modified), AFS |
| |
Potassium (K) |
mg/kg
(dry)
|
38 400.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Lanthanum (La) |
mg/kg
(dry)
|
26.2 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Magnesium (Mg) |
mg/kg
(dry)
|
18 500.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Manganese (Mn) |
mg/kg
(dry)
|
8 200.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Molybdenium (Mo) |
mg/kg
(dry)
|
6.3 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Sodium (Na) |
mg/kg
(dry)
|
13 200.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Niobium (Nb) |
mg/kg
(dry)
|
10.3 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Nickel (Ni) |
mg/kg
(dry)
|
53.3 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3683 (modified), EPA 200.8 (ICP-QMS/SFMS) |
| |
Phosphorus (P) |
mg/kg
(dry)
|
8 900.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Lead (Pb) |
mg/kg
(dry)
|
184.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3683 (modified), EPA 200.8 (ICP-QMS/SFMS) |
| |
Scandium (Sc) |
mg/kg
(dry)
|
7.3 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Silicon (Si) |
mg/kg
(dry)
|
192 000.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Tin (Sn) |
mg/kg
(dry)
|
<20 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Strontium (Sr) |
mg/kg
(dry)
|
549.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Titanium (Ti) |
mg/kg
(dry)
|
5 530.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Vanadium (V) |
mg/kg
(dry)
|
71.1 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Tungsten (W) |
mg/kg
(dry)
|
<60 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Yttrium (Y) |
mg/kg
(dry)
|
20.9 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Zinc (Zn) |
mg/kg
(dry)
|
1 790.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
| |
Zirconium (Zr) |
mg/kg
(dry)
|
217.0 |
0.0 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3682, EPA 200.7 (ICP-AES) |
Ash Properties
|
|
Proximate Analysis
|
| |
Moisture content |
wt%
(ar)
|
0.10 |
0.00 |
|
Analytica, Luleå |
2005-06-13 |
|
SS 02 81 13-1 |
| |
Loss on Ignition: LOI550 |
wt%
(dry)
|
6.30 |
0.00 |
|
Analytica, Luleå |
2005-06-13 |
|
Own method, 1000°C |
| |
Ash content at 815°C |
wt%
(dry)
|
93.70 |
0.00 |
|
Analytica, Luleå |
2005-06-13 |
|
Own method, 1000°C |
|
Ultimate Analysis
|
| |
Sulphur |
wt%
(dry)
|
1.22 |
0.00 |
|
Analytica, Luleå |
2005-06-13 |
|
ASTM D3683 (modified), EPA 200.7 (ICP-AES) |