Fuel Properties
|
|
Proximate Analysis
|
| |
Moisture content |
wt%
|
7.10 |
|
|
|
TUT |
|
CEN/TS 14774-1,2,3 |
|
| |
Volatile matter |
wt%
|
78.41 |
84.40 |
84.82 |
|
|
TUT |
|
|
|
| |
Ash content at 550°C |
wt%
|
0.46 |
0.50 |
|
|
|
TUT |
|
CEN/TS 14775 |
|
| |
Fixed carbon |
wt%
|
14.03 |
15.10 |
15.18 |
|
|
|
|
Calculated |
|
|
Ultimate Analysis
|
| |
Sulphur |
wt%
(dry)
|
<0.05 |
|
|
TUT |
|
CEN/TS15289 |
|
| |
Total (with halides) |
wt%
|
7.56 |
0.50 |
0.00 |
|
|
|
|
Calculated |
|
|
Calorific Values
|
| |
Net calorific value (LHV) |
MJ/kg
|
18.88 |
20.51 |
20.61 |
|
|
TUT |
|
CEN/TS 14918 |
|
| |
Gross calorific value (HHV) |
MJ/kg
|
16.42 |
17.67 |
17.76 |
|
|
TUT |
|
|
|
Physical Properties
|
|
Ash melting behaviour
|
| |
European standard method
|
| | |
SH (shrinkage temperature) |
°C
|
1 230 |
|
|
|
|
|
|
| | |
DEF (deformation temperature) |
°C
|
1 250 |
|
|
|
|
|
|
| | |
HE (hemispherical temperature) |
°C
|
1 290 |
|
|
|
|
|
|
| | |
FL (flow temperature) |
°C
|
1 330 |
|
|
|
|
|
|
|
Particle size distribution
|
| |
<0.25 mm |
wt%
|
12.00 |
|
|
|
|
CEN/TS 15149-1,2 |
|
| |
0.25-0.5 mm |
wt%
|
20.00 |
|
|
|
|
CEN/TS 15149-1,2 |
|
| |
0.5-1.0 mm |
wt%
|
38.00 |
|
|
|
|
CEN/TS 15149-1,2 |
|
| |
1.0-1.4 mm |
wt%
|
18.00 |
|
|
|
|
CEN/TS 15149-1,2 |
|
| |
1.4-2.0 mm |
wt%
|
9.40 |
|
|
|
|
CEN/TS 15149-1,2 |
|
| |
2.0-2.8 mm |
wt%
|
1.60 |
|
|
|
|
CEN/TS 15149-1,2 |
|
| |
2.8-3.15 mm |
wt%
|
0.10 |
|
|
|
|
CEN/TS 15149-1,2 |
|
| |
3.15-8 mm |
wt%
|
0.90 |
|
|
|
|
CEN/TS 15149-1,2 |
|