pyrolysis oil soybean cake (#2849)
| ID-number | #2849 |
|---|---|
| Material | pyrolysis oil soybean cake |
| Alternative name | pyrolysis oil soya bean cake |
| Classification | ECN Phyllis classification ▸ others ▸ non-fossil oil |
| NTA 8003 classification ▸ [800] samengestelde stromen ▸ [802] brandstof na pyrolyse | |
| Submitter organisation | ECN (Netherlands) |
| Submission date | 2009-07-06 |
| Remarks | Obtained at 400°C and 50°C/min heating rate from soybean oil cake (previous record). Viscosity at 50°C 72.38 cSt, flash point 63°C. Char composition in next record. Carbon analysis ASTM D 482; Hydrogen analysis ASTM D 3177; HHV by ASTM D 3286. |
| Literature | S. Sensöz, I. Kaynar: Bio-oil production from soybean (Glycine max L.); fuel properties of Bio-oil. Industrial Crops and Products 23 (2006) 99-105. |
Values
| Property | Unit | Value | Std dev | Det lim | Lab | Date | Method | Remarks | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ar | dry | daf | ||||||||||||||||||
Fuel Properties |
||||||||||||||||||||
Proximate Analysis |
||||||||||||||||||||
| Moisture content | wt% | 0.00 | ||||||||||||||||||
| Ash content | wt% | 0.00 | 0.00 | |||||||||||||||||
Ultimate Analysis |
||||||||||||||||||||
| Carbon | wt% | 67.89 | 67.89 | 67.89 | Measured | |||||||||||||||
| Hydrogen | wt% | 7.77 | 7.77 | 7.77 | Measured | |||||||||||||||
| Nitrogen | wt% | 10.84 | 10.84 | 10.84 | Measured | |||||||||||||||
| Oxygen | wt% | 13.50 | 13.50 | 13.50 | Calculated | |||||||||||||||
| Total (with halides) | wt% | 100.00 | 100.00 | 100.00 | Calculated | |||||||||||||||
Calorific Values |
||||||||||||||||||||
| Net calorific value (LHV) | MJ/kg | 31.90 | 31.90 | 31.90 | ||||||||||||||||
| Gross calorific value (HHV) | MJ/kg | 33.60 | 33.60 | 33.60 | ||||||||||||||||
| HHVMilne | MJ/kg | 30.50 | 30.50 | 30.50 | Calculated | |||||||||||||||
Physical Properties |
||||||||||||||||||||
Commonly used properties |
||||||||||||||||||||
| Bulk density (ar) | kg/m³ (ar) | 1 107 | ||||||||||||||||||