chicken manure (#1749)
| ID-number | #1749 |
|---|---|
| Material | chicken manure |
| Alternative name | poultry litter |
| Classification | ECN Phyllis classification ▸ manure ▸ poultry ▸ chicken manure |
| NTA 8003 classification ▸ [300] mest ▸ [310] pluimveemest | |
| Submitter organisation | ECN (Netherlands) |
| Submission date | 2000-07-06 |
| Literature | F.Anton, A.Andreas, P.Emmanuel, P.F.G.Michael and M.F.Suppan: Poultry litter as a fuel for a fluidised bed incinerator. In: Biomass for energy and industry. Proc. 1st World conference and exhibition, Sevilla, 5-9 June 2000 (Eds. S.Kyritsis et al.) |
Values
| Property | Unit | Value | Std dev | Det lim | Lab | Date | Method | Remarks | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ar | dry | daf | ||||||||||||||||||
Fuel Properties |
||||||||||||||||||||
Proximate Analysis |
||||||||||||||||||||
| Moisture content | wt% | 20.30 | ||||||||||||||||||
| Ash content | wt% | 23.99 | 30.10 | |||||||||||||||||
Ultimate Analysis |
||||||||||||||||||||
| Carbon | wt% | 26.74 | 33.55 | 48.00 | Measured | |||||||||||||||
| Hydrogen | wt% | 3.83 | 4.81 | 6.87 | Measured | |||||||||||||||
| Nitrogen | wt% | 2.27 | 2.85 | 4.07 | Measured | |||||||||||||||
| Sulphur | wt% | 0.20 | 0.25 | 0.36 | Measured | |||||||||||||||
| Oxygen | wt% | 22.63 | 28.39 | 40.62 | Calculated | |||||||||||||||
| Total (with halides) | wt% | 99.96 | 99.95 | 99.92 | Calculated | |||||||||||||||
Calorific Values |
||||||||||||||||||||
| Net calorific value (LHV) | MJ/kg | 8.90 | 11.79 | 16.87 | ||||||||||||||||
| Gross calorific value (HHV) | MJ/kg | 10.23 | 12.84 | 18.37 | ||||||||||||||||
| HHVMilne | MJ/kg | 10.95 | 13.74 | 19.66 | Calculated | |||||||||||||||
Chemical Analyses |
||||||||||||||||||||
Halides |
||||||||||||||||||||
| Chlorine (Cl) | mg/kg (dry) | 500.0 | ||||||||||||||||||
Physical Properties |
||||||||||||||||||||
Ash melting behaviour |
||||||||||||||||||||
American standard method, measured in oxidizing conditions |
||||||||||||||||||||
| IDT (initial deformation temperature) | °C | 1 120 | ||||||||||||||||||
| FT (fluid temperature) | °C | 1 220 | ||||||||||||||||||
Ash Properties |
||||||||||||||||||||
Ash composition |
||||||||||||||||||||
| SO3 | wt% (ash) | 2.23 | ||||||||||||||||||
| Cl | wt% (ash) | 0.99 | ||||||||||||||||||
| P2O5 | wt% (ash) | 8.88 | ||||||||||||||||||
| SiO2 | wt% (ash) | 11.75 | ||||||||||||||||||
| Fe2O3 | wt% (ash) | 3.47 | ||||||||||||||||||
| Al2O3 | wt% (ash) | 3.24 | ||||||||||||||||||
| CaO | wt% (ash) | 54.50 | ||||||||||||||||||
| MgO | wt% (ash) | 5.44 | ||||||||||||||||||
| Na2O | wt% (ash) | 0.18 | ||||||||||||||||||
| K2O | wt% (ash) | 8.77 | ||||||||||||||||||
| Cu | mg/kg (ash) | 0.0 | ||||||||||||||||||
| Mn | mg/kg (ash) | 0.1 | ||||||||||||||||||
| Cr | mg/kg (ash) | 0.0 | ||||||||||||||||||