chicken manure (#1748)
| ID-number | #1748 |
|---|---|
| Material | chicken manure |
| Alternative name | poultry litter |
| Classification | ECN Phyllis classification ▸ manure ▸ poultry ▸ chicken manure |
| NTA 8003 classification ▸ [300] mest ▸ [310] pluimveemest | |
| Submitter organisation | ECN (Netherlands) |
| Submission date | 2000-07-06 |
| Literature | F.Anton, A.Andreas, P.Emmanuel, P.F.G.Michael and M.F.Suppan: Poultry litter as a fuel for a fluidised bed incinerator. In: Biomass for energy and industry. Proc. 1st World conference and exhibition, Sevilla, 5-9 June 2000 (Eds. S.Kyritsis et al.) |
Values
| Property | Unit | Value | Std dev | Det lim | Lab | Date | Method | Remarks | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ar | dry | daf | ||||||||||||||||||
Fuel Properties |
||||||||||||||||||||
Proximate Analysis |
||||||||||||||||||||
| Moisture content | wt% | 75.20 | ||||||||||||||||||
| Ash content | wt% | 10.43 | 42.06 | |||||||||||||||||
Ultimate Analysis |
||||||||||||||||||||
| Carbon | wt% | 7.07 | 28.51 | 49.20 | Measured | |||||||||||||||
| Hydrogen | wt% | 1.11 | 4.48 | 7.72 | Measured | |||||||||||||||
| Nitrogen | wt% | 0.69 | 2.78 | 4.80 | Measured | |||||||||||||||
| Sulphur | wt% | 0.14 | 0.56 | 0.97 | Measured | |||||||||||||||
| Oxygen | wt% | 5.31 | 21.41 | 36.95 | Calculated | |||||||||||||||
| Total (with halides) | wt% | 99.95 | 99.80 | 99.66 | Calculated | |||||||||||||||
Calorific Values |
||||||||||||||||||||
| Net calorific value (LHV) | MJ/kg | 0.61 | 9.86 | 17.02 | ||||||||||||||||
| Gross calorific value (HHV) | MJ/kg | 2.69 | 10.84 | 18.70 | ||||||||||||||||
| HHVMilne | MJ/kg | 3.08 | 12.40 | 21.40 | Calculated | |||||||||||||||
Chemical Analyses |
||||||||||||||||||||
Halides |
||||||||||||||||||||
| Chlorine (Cl) | mg/kg (dry) | 2 000.0 | ||||||||||||||||||
Physical Properties |
||||||||||||||||||||
Ash melting behaviour |
||||||||||||||||||||
American standard method, measured in oxidizing conditions |
||||||||||||||||||||
| IDT (initial deformation temperature) | °C | 1 100 | ||||||||||||||||||
| FT (fluid temperature) | °C | 1 240 | ||||||||||||||||||
Ash Properties |
||||||||||||||||||||
Ash composition |
||||||||||||||||||||
| SO3 | wt% (ash) | 1.80 | ||||||||||||||||||
| Cl | wt% (ash) | 0.78 | ||||||||||||||||||
| P2O5 | wt% (ash) | 14.06 | ||||||||||||||||||
| SiO2 | wt% (ash) | 8.10 | ||||||||||||||||||
| Fe2O3 | wt% (ash) | 2.88 | ||||||||||||||||||
| Al2O3 | wt% (ash) | 2.36 | ||||||||||||||||||
| CaO | wt% (ash) | 51.05 | ||||||||||||||||||
| MgO | wt% (ash) | 6.05 | ||||||||||||||||||
| Na2O | wt% (ash) | 1.54 | ||||||||||||||||||
| K2O | wt% (ash) | 10.78 | ||||||||||||||||||
| Cu | mg/kg (ash) | 0.0 | ||||||||||||||||||
| Mn | mg/kg (ash) | 0.1 | ||||||||||||||||||