peat (#1407)
| ID-number | #1407 |
|---|---|
| Material | peat |
| Classification | ECN Phyllis classification ▸ fossil fuel ▸ peat ▸ peat |
| NTA 8003 classification ▸ [800] samengestelde stromen | |
| Submitter organisation | ECN (Netherlands) |
| Submission date | 1999-03-12 |
| Literature | B. Skrifvars, R. Zevenhoven, M. Frankenhaeuser and M. Hupa: Sintering of ashes from PDF co-combustion with peat, wood and bark. In: Finnish-Swedish Flame Days 1996, September 3-4, Naantali, Finland (1996). |
Values
| Property | Unit | Value | Std dev | Det lim | Lab | Date | Method | Remarks | ||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ar | dry | daf | ||||||||||||||||||
Main biomass properties |
||||||||||||||||||||
Proximate analysis |
||||||||||||||||||||
| Moisture content | wt% | 29.80 | ||||||||||||||||||
| Ash content | wt% | 4.42 | 6.30 | |||||||||||||||||
| Volatile matter | wt% | 47.81 | 68.10 | 72.68 | ||||||||||||||||
| Fixed carbon | wt% | 17.97 | 25.60 | 27.32 | Calculated | |||||||||||||||
Ultimate analysis (macroelements) |
||||||||||||||||||||
| Carbon | wt% | 37.42 | 53.30 | 56.88 | Measured | |||||||||||||||
| Hydrogen | wt% | 3.93 | 5.60 | 5.98 | Measured | |||||||||||||||
| Oxygen | wt% | 23.27 | 33.15 | 35.38 | Calculated | |||||||||||||||
| Nitrogen | wt% | 1.00 | 1.43 | 1.53 | Measured | |||||||||||||||
| Sulphur | wt% | 0.11 | 0.16 | 0.17 | Measured | |||||||||||||||
| Total (with halides) | wt% | 100.00 | 100.00 | 100.00 | Calculated | |||||||||||||||
Halides |
||||||||||||||||||||
| Chlorine (Cl) | mg/kg | 421.2 | 600.0 | 640.3 | Measured | |||||||||||||||
Heating value |
||||||||||||||||||||
| Net calorific value (LHV) | MJ/kg | 13.31 | 20.00 | 21.34 | ||||||||||||||||
| Gross calorific value (HHV) | MJ/kg | 14.90 | 21.22 | 22.65 | ||||||||||||||||
| HHVMilne | MJ/kg | 14.99 | 21.35 | 22.79 | Calculated | |||||||||||||||
Ash Properties |
||||||||||||||||||||
Ash composition |
||||||||||||||||||||
| SiO2 | wt% (ash) | 44.30 | ||||||||||||||||||
| Fe2O3 | wt% (ash) | 8.08 | ||||||||||||||||||
| Al2O3 | wt% (ash) | 22.50 | ||||||||||||||||||
| CaO | wt% (ash) | 10.40 | ||||||||||||||||||
| MgO | wt% (ash) | 3.45 | ||||||||||||||||||