wood, willow (#1305)
ID-number | #1305 |
---|---|
Material | wood, willow |
Classification | ECN Phyllis classification ▸ untreated wood ▸ willow ▸ wood, willow |
NTA 8003 classification ▸ [100] hout ▸ [110] vers hout ▸ [120] loofhout ▸ [122] zacht loofhout | |
Ash type | 550 degC |
Submitter organisation | ECN (Netherlands) |
Submission date | 1998-08-21 |
Literature | ECN laboratories. |
Values
Property | Unit | Value | Std dev | Det lim | Lab | Date | Method | Remarks | ||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
ar | dry | daf | ||||||||||||||||||
Main biomass properties |
||||||||||||||||||||
Proximate analysis |
||||||||||||||||||||
Moisture content | wt% (ar) | |||||||||||||||||||
Ash content | wt% | 4.59 | ||||||||||||||||||
Ultimate analysis (macroelements) |
||||||||||||||||||||
Total (with halides) | wt% | 4.59 | 0.00 | Calculated | ||||||||||||||||
Ash melting behaviour |
||||||||||||||||||||
American standard method, measured in reducing conditions |
||||||||||||||||||||
IDT (initial deformation temperature) | °C | 1 482 | ||||||||||||||||||
SOT (softening or spherical temperature) | °C | 1 492 | ||||||||||||||||||
HT (hemispherical temperature) | °C | 1 504 | ||||||||||||||||||
FT (fluid temperature) | °C | 1 516 | ||||||||||||||||||
Ash Properties |
||||||||||||||||||||
Ash composition |
||||||||||||||||||||
CO2 | wt% (ash) | 2.20 | ||||||||||||||||||
SO3 | wt% (ash) | 3.20 | ||||||||||||||||||
Cl | wt% (ash) | 0.75 | ||||||||||||||||||
P2O5 | wt% (ash) | 10.20 | ||||||||||||||||||
SiO2 | wt% (ash) | 2.30 | ||||||||||||||||||
Fe2O3 | wt% (ash) | 0.33 | ||||||||||||||||||
Al2O3 | wt% (ash) | 0.35 | ||||||||||||||||||
CaO | wt% (ash) | 37.20 | ||||||||||||||||||
MgO | wt% (ash) | 4.80 | ||||||||||||||||||
Na2O | wt% (ash) | 2.80 | ||||||||||||||||||
K2O | wt% (ash) | 12.10 | ||||||||||||||||||
TiO2 | wt% (ash) | 0.03 |